3D Blend Hi-Speed Resin (Grey, 1kg)

Description

3D Blend Hi-Speed Resin has a very low viscosity (50–100 mPa·s) so it flows back under the plate almost instantly, allowing short exposures and fast lifts. On high-speed printers it prints up to three times faster than standard resin.

It also has the best impact strength of our standard resins, so fast prints are not fragile prints.

Key features

• Up to 3× faster on high-speed printers with ACF film
• Very low viscosity — 50–100 mPa·s, quick recoat and easy draining
• Tough — 101 J/m notched impact, 9.3% elongation
• Fine detail and smooth surfaces
• Tested on Anycubic M5s and ELEGOO Saturn 4 Ultra class printers

Applications

• Fast prototyping and iteration
• Batch printing of figures and parts
• Print farms and service bureaus

Product information

Item	Detail
Product	3D Blend Hi-Speed Resin
Type	High-speed standard photopolymer resin (FR-A series)
Colour	Grey
Net weight	1 kg
Wavelength	385–405 nm
Compatible printers	LCD, MSLA and DLP resin printers (Elegoo, Anycubic, Phrozen, Creality, Uniformation, Bambu and others)

Technical data

Property	Value
Tensile strength	42.8 MPa
Tensile modulus	518 MPa
Elongation at break	9.3%
Flexural strength	47.5 MPa
Flexural modulus	1284 MPa
Notched Izod impact	101 J/m
Hardness	80–86 Shore D
Viscosity (25 °C)	50–100 mPa·s
Density	1.05–1.25 g/cm³

Manufacturer test data (ASTM D638 / D790 / D256 / D2240, post-cured at 405 nm, 23 °C). Values ±10%.

How to print

1. Bring resin and room to 20–30 °C — cold resin is thick and causes failed prints
2. Shake the bottle for 1–2 minutes (or roll it) until no sediment remains
3. Check the FEP/ACF film for holes and clean the build plate; level the plate if needed
4. Pour resin into the vat up to the MAX line
5. In your slicer (Chitubox, Lychee, etc.) enter the print settings below, orient parts at 30–45° and add supports
6. Hollow large models (2–3 mm wall) and add drain holes to save resin and avoid suction
7. Run an exposure test (e.g. RERF or validation matrix) the first time you use this resin on your printer
8. Print, then let the plate drip for 10–15 min before removing parts

Recommended print settings (UV exposure)

Setting	Starting value
Layer height	0.05 mm
Bottom layers	4–6
Lift distance	6 mm (8–10 mm on 7–10″ screens, 11–15 mm on 10–15″ screens)
Lift speed	60–80 mm/min
Retract speed	150 mm/min
Wavelength	385–410 nm
Bottom exposure (standard printer)	15–20 s
Layer exposure (standard printer)	2–2.5 s
Bottom exposure (high-speed printer, ACF film)	25–30 s
Layer exposure (high-speed printer, ACF film)	1.8 s
Lift distance (ACF film)	3 mm

Starting values tested on a 6.6″ mono LCD (3500–4500 µW/cm²). Adjust for your printer’s light power: a stronger screen needs shorter exposure; a weaker or ageing screen needs longer.

Washing

1. Remove the build plate and let excess resin drip back into the vat (10–15 min)
2. Wash in IPA (95%+) for 2–3 min, then in a second, cleaner IPA bath for 1–2 min — do not exceed 10 min in total
3. Remove supports while the part is still slightly soft for cleaner marks
4. Dry completely with compressed air or leave 15–30 min — curing a wet part causes white haze

UV post-curing (polymerization)

Parameter	Value
Wavelength	405 nm (385–410 nm)
High-power curing box (≈200 mW/cm²)	1 min per side, in water
Standard curing station (40–60 W)	2–4 min, rotating
Sunlight	10–20 min, rotating
Note	Over-curing makes standard resin brittle — stop once the surface is no longer tacky

Storage & safety

• Store sealed in the original bottle at 15–30 °C, away from sunlight, heat sources and moisture
• Shake or roll the bottle for 1–2 minutes before every print — pigments and fillers settle
• Shelf life: 24 months unopened (18 months for dental resins)
• Wear nitrile gloves and safety glasses; work in a ventilated room
• Skin contact: wash with soap and water. Eye contact: rinse 15 min and seek medical advice
• Dispose of uncured resin and contaminated IPA as chemical waste, never in the drain

In the box

1 × 3D Blend Hi-Speed Resin (Grey), 1 kg bottle.